Retained austenite decomposition and carbide precipitation during isothermal tempering of a medium-carbon low-alloy bainitic steel

Downloads

Downloads per month over past year

Talebi, Seyyed Hesamondin, Jahazi, Mohammad et Melkonyan, Haikouhi. 2018. « Retained austenite decomposition and carbide precipitation during isothermal tempering of a medium-carbon low-alloy bainitic steel ». Materials, vol. 11, nº 8.
Compte des citations dans Scopus : 2.

[img]
Preview
PDF
Jahazi M 2018 17315.pdf - Published Version
Use licence: Creative Commons CC BY.

Download (14MB) | Preview

Abstract

The effect of isothermal tempering on retained austenite decomposition and carbide precipitation were investigated in a medium-carbon low-alloy bainitic steel. High-resolution dilatometry was used to perform isothermal tempering at 350 °C, 550 °C and 600 °C for different holding times up to 16 h. The decomposition of retained austenite, morphology and composition of carbides were investigated by analyzing the dilatometric curves and were confirmed through scanning and transmission electron microscopy observations. The decomposition behavior of retained austenite varied significantly as a function of the tempering temperature with a full decomposition observed at 600 °C. It was also found that by increasing the tempering temperature from 550 °C to 600 °C, carbides precipitate approximately twice as fast, and evolve from M3C type to Cr7C3 and Cr23C6 after 16 h of tempering at 600 °C.

Item Type: Peer reviewed article published in a journal
Professor:
Professor
Jahazi, Mohammad
Affiliation: Génie mécanique
Date Deposited: 10 Sep 2018 20:13
Last Modified: 03 Jun 2019 18:44
URI: https://espace2.etsmtl.ca/id/eprint/17315

Actions (login required)

View Item View Item