Loucif, A., Bitterlin, M., Jahazi, M., Tremblay, R., Morin, J. B. et Lapierre-Boire, L. P..
2017.
« Crack analysis in as cast large size ingot of a high strength steel ».
In 14th International Conference on Fracture (ICF 2017) (Rhodes, Greece, June 18-20, 2017)
pp. 766-767.
International Conference on Fracture.
Prévisualisation |
PDF
Jahazi-M-2017-18887.pdf - Version acceptée Licence d'utilisation : Tous les droits réservés aux détenteurs du droit d'auteur. Télécharger (316kB) | Prévisualisation |
Résumé
The mechanism of crack apparition of an as cast high strength low alloy steel ingot was investigated. Elemental, mechanical and crystallographic analyses proved that tensile stresses accumulated during casting and annealing are responsible of crack generation. The crack propagation is favored by the formation of chromium carbides at prior aus-tenite grain boundaries.
| Type de document: | Compte rendu de conférence |
|---|---|
| Professeur: | Professeur Jahazi, Mohammad |
| Affiliation: | Génie mécanique |
| Date de dépôt: | 17 juin 2019 18:09 |
| Dernière modification: | 13 avr. 2023 16:08 |
| URI: | https://espace2.etsmtl.ca/id/eprint/18887 |
Actions (Authentification requise)
 |
Dernière vérification avant le dépôt |