Rajakrishnan, Navneeth, Sadeghifar, Morteza, Bhattacharjee, Pinaki, Champliaud, Henri et Jahazi, Mohammad.
2025.
« Kinetics of austenite formation in a medium-carbon, low-alloy steel with an initial martensite microstructure: Influence of prior austenite grain size ».
Journal of Manufacturing and Materials Processing, vol. 9, nº 1.
Compte des citations dans Scopus : 1.
Prévisualisation |
PDF
Champliaud-H-2025-30524.pdf - Version publiée Licence d'utilisation : Creative Commons CC BY. Télécharger (7MB) | Prévisualisation |
Résumé
The impact of prior austenite grain size (PAGS) on the kinetics of austenite formation with an initial martensite microstructure was investigated in a medium-carbon, low-alloy steel. Two distinct PAGS of 117 and 330 μm, representing the range of grain sizes encountered in industries, were considered. In this analysis, high-resolution dilatometry was used to study the formation of austenite during continuous heating experiments. The analysis of the dilatometry results revealed that grain refinement accelerated the rate of austenite formation without impacting its austenite formation temperature. Intermittent quenching tests were conducted to elucidate the nucleation and growth mechanisms of austenite formation using a combination of optical, scanning electron microscopy (SEM), and electron backscatter diffraction (EBSD). The differences in austenite formation kinetics as a function of prior austenite grain size were quantified and modeled in the framework of diffusion-controlled nucleation and growth theories using the genetic algorithm optimization.
Type de document: | Article publié dans une revue, révisé par les pairs |
---|---|
Professeur: | Professeur Champliaud, Henri Jahazi, Mohammad |
Affiliation: | Génie mécanique, Génie mécanique |
Date de dépôt: | 13 févr. 2025 16:41 |
Dernière modification: | 04 mars 2025 14:58 |
URI: | https://espace2.etsmtl.ca/id/eprint/30524 |
Actions (Authentification requise)
![]() |
Dernière vérification avant le dépôt |