Rodrigues, Samuel F., Siciliano, Fulvio, Aranas Jr., Clodualdo, Silva, Eden S., Reis, Gedeon S., Jahazi, Mohammad et Jonas, John J..
2019.
« Dynamic phase transformation behavior of a Nb-microalloyed steel during roughing passes at temperatures above the Ae3 ».
Metals, vol. 9, nº 3.
Compte des citations dans Scopus : 6.
Prévisualisation |
PDF
Jahazi M 2019 18841.pdf - Version publiée Licence d'utilisation : Creative Commons CC BY. Télécharger (3MB) | Prévisualisation |
Résumé
A five-pass torsion simulation of the roughing passes applied during hot plate rolling was performed in the single-phase austenite region of a Nb-microalloyed steel under continuous cooling conditions. The deformation temperatures were approximately half-way between the Ae3 and the delta ferrite formation temperature (i.e., 250 °C above the Ae3) in which the free energy difference of austenite and ferrite is at maximum. The microstructures in-between passes were analyzed to characterize and quantify the occurrence of deformation-induced dynamic phase transformation. It was observed that about 7% of austenite transforms into ferrite right after the final pass. The results are consistent with the calculated critical strains and driving forces which indicate that dynamic transformation (DT) can take place at any temperature above the Ae3. This mechanism occurs even with the presence of high Nb in the material, which is known to retard and hinder the occurrence of DT by means of pinning and solute drag effects. The calculated cooling rate during quenching and the time–temperature–transformation curves of the present material further verified the existence of dynamically transformed ferrite.
| Type de document: | Article publié dans une revue, révisé par les pairs |
|---|---|
| Professeur: | Professeur Jahazi, Mohammad |
| Affiliation: | Génie mécanique |
| Date de dépôt: | 03 juin 2019 21:02 |
| Dernière modification: | 13 avr. 2023 16:08 |
| URI: | https://espace2.etsmtl.ca/id/eprint/18841 |
Actions (Authentification requise)
 |
Dernière vérification avant le dépôt |