Mohan, Nirupama et Chaudhari, Gajanan.
2025.
« Corrosion performance of boronized martensitic stainless steels ».
In Proceedings of the CSME-CFDSC-CSR 2025 International Congress (Montreal, QC, Canada, May 25-28, 2025)
Coll. « Progress in Canadian Mechanical Engineering », vol. 8.
https://doi.org/10.82417/vpe6-7h89 :
Prévisualisation |
PDF
591 - Corrosion performance of boronized.pdf - Version publiée Licence d'utilisation : Tous les droits réservés aux détenteurs du droit d'auteur. Télécharger (990kB) | Prévisualisation |
Résumé
13Cr-4Ni and 16Cr-5Ni martensite stainless steels were pack boronized at 950 and 1000 °C. These samples were further tempered at 600 °C for 2 h. Pack boronizing lead to the development of boride layer on the MSS substrate. Immersion tests were conducted in 0.1 M H2SO4 and 0.06 M HCl media. SEM micrographs reveal the surface morphology of all the samples post immersion tests. Potentiodynamic polarization tests were also conducted in 0.6 M NaCl solution. Boronized samples show a reduction in weight loss as compared to their bare counterparts in the given immersion media. However, the polarization curves demonstrate inferior corrosion performance of the boronized samples.
| Type de document: | Compte rendu de conférence |
|---|---|
| Éditeurs: | Éditeurs ORCID Hof, Lucas A. NON SPÉCIFIÉ Di Labbio, Giuseppe NON SPÉCIFIÉ Tahan, Antoine NON SPÉCIFIÉ Sanjosé, Marlène NON SPÉCIFIÉ Lalonde, Sébastien NON SPÉCIFIÉ Demarquette, Nicole R. NON SPÉCIFIÉ |
| Date de dépôt: | 18 déc. 2025 15:16 |
| Dernière modification: | 18 déc. 2025 15:16 |
| URI: | https://espace2.etsmtl.ca/id/eprint/32461 |
Actions (Authentification requise)
 |
Dernière vérification avant le dépôt |